Grade | GC-1250 | |
树脂种类 | PC/ABS |
Flame Retardant, Laptop |
项目 | 测试方法 | 条件 | 单位 | 代表值 |
---|
物理性质 | ||||
---|---|---|---|---|
比重 | ASTM D792 | Natural 或代表 color | - | 1.39 |
熔融指数 | ASTM D1238 | 250℃, 5kg | g/10min | 30 |
熔融指数 | ASTM D1238 | 250℃, 2.16kg | g/10min | - |
成型收缩率(MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.15 - 0.45 |
成型收缩率(TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.15 - 0.45 |
ASH content | ASTM D5630 | - | % | 24.5 |
机械性质 | ||||
---|---|---|---|---|
拉伸强度(at yield) | ASTM D638 | 5mm/min | kgf/cm2 | 520 |
伸长率(at break) | ASTM D638 | 5mm/min | % | 15 |
拉伸模量35000 | ASTM D638 | 5mm/min | kgf/cm2 | 35000 |
断裂强度(at break) | ASTM D638 | 5mm/min | kgf/cm2 | 500 |
弯曲强度 | ASTM D790 | 2.8mm/min | kgf/cm2 | 900 |
弯曲模量 | ASTM D790 | 2.8mm/min | kgf/cm2 | 50000 |
Izod冲击强度(notched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 7 |
Izod冲击强度(notched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 8 |
硬度 | ASTM D785 | R-Scale | - | 110 |
热学特性 | ||||
---|---|---|---|---|
热变形温度 | ASTM D648 | 18.56kgf/cm2, 6.4mm | °C | 88 |
热变形温度 | ASTM D648 | 4.6kgf/cm2, 6.4mm | °C | - |
维卡软化温度 | ISO 306 | B/50 | °C | 97 |
阻燃 | ||||
---|---|---|---|---|
阻燃度 | UL94 | V-0 | mm | 1.2, 3.0 |