Grade | IN-3100G | |
树脂种类 | PC/GF |
项目 | 测试方法 | 条件 | 单位 | 代表值 |
---|
物理性质 | ||||
---|---|---|---|---|
比重 | ASTM D792 | Natural 或代表 color | - | 1.24 |
熔融指数 | ASTM D1238 | 250℃, 10kg | g/10min | 23 |
熔融指数 | ASTM D1238 | 300℃, 1.2kg | g/10min | 12 |
成型收缩率(MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.3-0.6 |
成型收缩率(TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.4-0.7 |
ASH content | ASTM D5630 | - | % | 10 |
机械性质 | ||||
---|---|---|---|---|
拉伸强度(at yield) | ASTM D638 | 5mm/min | kgf/cm2 | 530 |
伸长率(at break) | ASTM D638 | 5mm/min | % | 8 |
拉伸模量- | ASTM D638 | 5mm/min | kgf/cm2 | - |
断裂强度(at break) | ASTM D638 | 5mm/min | kgf/cm2 | 530 |
弯曲强度 | ASTM D790 | 2.8mm/min | kgf/cm2 | 900 |
弯曲模量 | ASTM D790 | 2.8mm/min | kgf/cm2 | 34000 |
Izod冲击强度(notched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 15 |
Izod冲击强度(notched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 21 |
硬度 | ASTM D785 | R-Scale | - | - |
热学特性 | ||||
---|---|---|---|---|
热变形温度 | ASTM D648 | 18.56kgf/cm2, 6.4mm | °C | 138 |
热变形温度 | ASTM D648 | 4.6kgf/cm2, 6.4mm | °C | - |
阻燃 | ||||
---|---|---|---|---|
阻燃度 | UL94 | HB | mm | 0.8, 3.0 |