Grade | TK-2050HP |
| 树脂种类 | PCT/GF |
| E&E, General |
| 项目 | 测试方法 | 条件 | 单位 | 代表值 |
|---|
| 物理性质 | ||||
|---|---|---|---|---|
| 比重 | ASTM D792 | Natural 或代表 color | - | 1.71 |
| 熔融指数 | ASTM D1238 | 300℃, 1.2kg | g/10min | 18 |
| 成型收缩率(MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.4-0.7 |
| 成型收缩率(TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.4-0.7 |
| ASH content | ASTM D5630 | - | % | 46.0 |
| 机械性质 | ||||
|---|---|---|---|---|
| 拉伸强度(at yield) | ASTM D638 | 5mm/min | kgf/cm2 | 600 |
| 伸长率(at break) | ASTM D638 | 5mm/min | % | 2.1 |
| 拉伸模量35,000 | ASTM D638 | 5mm/min | kgf/cm2 | 35,000 |
| 断裂强度(at break) | ASTM D638 | 5mm/min | kgf/cm2 | 600 |
| 弯曲强度 | ASTM D790 | 2.8mm/min | kgf/cm2 | 850 |
| 弯曲模量 | ASTM D790 | 2.8mm/min | kgf/cm2 | 53,000 |
| Izod冲击强度(notched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 1.9 |
| Izod冲击强度(notched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 2.5 |
| Izod冲击强度(unnotched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 19 |
| Izod冲击强度(unnotched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 25 |
| 硬度 | ASTM D785 | R-Scale | - | - |
| 热学特性 | ||||
|---|---|---|---|---|
| 热变形温度 | ASTM D648 | 18.56kgf/cm2, 6.4mm | °C | 195 |
| 阻燃 | ||||
|---|---|---|---|---|
| 阻燃度 | UL94 | HB | mm | 1.5, 3.0 |
| 光学性质 | ||||
|---|---|---|---|---|
| 初期反射率 | E 1331 | % | 93.5↑ | |