Grade | UH-1064 |
| 树脂种类 | PC |
| 项目 | 测试方法 | 条件 | 单位 | 代表值 |
|---|
| 物理性质 | ||||
|---|---|---|---|---|
| 比重 | ASTM D792 | Natural 或代表 color | - | 1.19 |
| 熔融指数 | ASTM D1238 | 300℃, 1.2kg | g/10min | 16 |
| 成型收缩率(MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.4-0.7 |
| 成型收缩率(TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.4-0.7 |
| 机械性质 | ||||
|---|---|---|---|---|
| 拉伸强度(at yield) | ASTM D638 | 50mm/min | kgf/cm2 | 600 |
| 伸长率(at break) | ASTM D638 | 50mm/min | % | 90 |
| 拉伸模量20000 | ASTM D638 | 50mm/min | kgf/cm2 | 20000 |
| 断裂强度(at break) | ASTM D638 | 50mm/min | kgf/cm2 | 550 |
| 弯曲强度 | ASTM D790 | 2.8mm/min | kgf/cm2 | 850 |
| 弯曲模量 | ASTM D790 | 2.8mm/min | kgf/cm2 | 21000 |
| Izod冲击强度(notched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 45 |
| Izod冲击强度(notched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 75 |
| 硬度 | ASTM D785 | R-Scale | - | 118 |
| 热学特性 | ||||
|---|---|---|---|---|
| 热变形温度 | ASTM D648 | 18.56kgf/cm2, 6.4mm | °C | 123 |
| 热变形温度 | ASTM D648 | 4.6kgf/cm2, 6.4mm | °C | - |
| 维卡软化温度 | ISO 306 | B/50 | °C | 138 |
| 阻燃 | ||||
|---|---|---|---|---|
| 阻燃度 | UL94 | V-0 | mm | 1.5, 3.0 |
1. 上述数值为NP基准代表值，根据不同颜色可能会有偏差，仅限适用于选定材料为目的
2. 上述数值为选定材料的基础指导，不作为材料正式规格，不适用于模具设计
3. 上述数值可根据实际加工条件进行适当调整和使用，使用范围即最终成品不出现异常状态为止