Grade | WR-9300HF | |
树脂种类 | ASA |
Automotive |
项目 | 测试方法 | 条件 | 单位 | 代表值 |
---|
物理性质 | ||||
---|---|---|---|---|
比重 | ASTM D792 | Natural 或代表 color | - | 1.07 |
熔融指数 | ASTM D1238 | 220℃, 10kg | g/10min | 12 |
熔融指数 | ASTM D1238 | 250℃, 2.16kg | g/10min | 6.5 |
成型收缩率(MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.4-0.7 |
成型收缩率(TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.4-0.7 |
机械性质 | ||||
---|---|---|---|---|
拉伸强度(at yield) | ASTM D638 | 5mm/min | kgf/cm2 | 450 |
伸长率(at break) | ASTM D638 | 5mm/min | % | 15 |
拉伸模量- | ASTM D638 | 5mm/min | kgf/cm2 | - |
断裂强度(at break) | ASTM D638 | 5mm/min | kgf/cm2 | - |
弯曲强度 | ASTM D790 | 2.8mm/min | kgf/cm2 | 680 |
弯曲模量 | ASTM D790 | 2.8mm/min | kgf/cm2 | 22000 |
Izod冲击强度(notched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 10 |
Izod冲击强度(notched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 15 |
Izod冲击强度(notched) | ASTM D256 | 1/4 inch at -30°C | kgf·cm/cm | 4.5 |
Izod冲击强度(notched) | ASTM D256 | 1/8 inch at -30°C | kgf·cm/cm | 3.5 |
硬度 | ASTM D785 | R-Scale | - | 106 |
热学特性 | ||||
---|---|---|---|---|
热变形温度 | ASTM D648 | 18.56kgf/cm2, 6.4mm | °C | 87 |
热变形温度 | ASTM D648 | 4.6kgf/cm2, 6.4mm | °C | 92 |
热变形温度 | ASTM D648 | 18.56kgf/cm2, 3.2mm | °C | 73 |
热变形温度 | ASTM D648 | 4.6kgf/cm2, 3.2mm | °C | 86 |
维卡软化温度 | ISO 306 | B/50 | °C | 100 |