DATASHEET COMPARISON

ASTM Property

ASTM Property ISO Property
logo_infino Grade QC-1220UR
Resin Type PC
부가 설명
Outdoor Housing
Item Measuring Method Condition Unit Value
물리적 성질
Physical
Specific Gravity ASTM D792 Natural or representative color - 1.2
Melt Flow Index ASTM D1238 300℃, 1.2kg g/10min 22
Mold Shrinkage(MD) ASTM D955 Flow at 3.2mm(MD) % 0.4-0.7
Mold Shrinkage(MD) ASTM D955 X-Flow at 3.2mm(TD) % 0.4-0.7
기계적 성질
Mechanical
Tensile Strength at Yield ASTM D638 50mm/min kgf/cm2 640
Tensile Strain at break ASTM D638 50mm/min % 110
Tensile Modulus20000 ASTM D638 50mm/min kgf/cm2 20000
Tensile Strength at break ASTM D638 50mm/min kgf/cm2 600
Flexural Strength ASTM D790 2.8mm/min kgf/cm2 920
Flexural Modulus ASTM D790 2.8mm/min kgf/cm2 23000
Izod Impact Strength(notched) ASTM D256 1/4 inch at 23°C kgf·cm/cm 10
Izod Impact Strength(notched) ASTM D256 1/8 inch at 23°C kgf·cm/cm 9
Rockwell Hardness ASTM D785 R-Scale - 120
열적 성질
Thermal
Heat Deflection Temperature ASTM D648 18.56kgf/cm2, 6.4mm °C 125
Heat Deflection Temperature ASTM D648 4.6kgf/cm2, 6.4mm °C 136
VICAT Softening Temperature ISO 306 B/50 °C 140
RTI, Ele UL 746B 1.6, - °C 130
RTI, Imp UL 746B 1.6, - °C 125
RTI, Str UL 746B 1.6, - °C 125
flame retardant
Flammability
Flammability UL94 V-2 mm 1.0, 1.6, 3.2
Glow-Wire Flammability Index IEC 60695-2-12 1.0, 1.6, 3.2 °C 850, 850, 850
Glow-Wire Ignition Index IEC 60695-2-13 1.0, 1.6, 3.2 °C 875, 900, 875
UV light exposure/water immersion UL 746C - - f1
electrical feature
Electric
Volume Resistivity ASTM D257 at 23°C, 50% RH Ωcm 1.0E+16
Hot Wire Ignition UL746A 1.0, 1.6, 3.2 PLC 0, 3, 2
High Current Arc Ignition UL746A 1.0, 1.6, 3.2 PLC 0, 0, 0
Comparative Tracking Index IEC 60112 - PLC 0
High Voltage Arc Tracking Rate UL746A - PLC 2
High Volt, Low Current Arc Resis UL746A - PLC 5
1. The above figures are the representative values based on NP, which may vary from color to color, and can be used as a reference only for the purpose of selecting materials. 2. The above figures are basic guidelines for selecting materials; therefore, they are not regarded as the official specifications for materials involved, and cannot be used for the purpose of designing a mold. 3. The above values can be adjusted in accordance with processing conditions, and the specific change in value is allowed only within a limited range in which adjustment has no adverse or negative impact on the final product.
Information inserted in this document such as data, statements, representative values, etc. are provided solely for customer convenience. It does not expressly or impliedly guarantee anything regarding the safety or practicability of the (1) materials, (2) products, and/or (3) design that utilizes recommendations or proposals, of LOTTE Chemical. Furthermore, nothing in the contents of this document shall have any legal binding effect, and especially, the representative value is simply for reference and is not a minimum value that has legal binding effect.
Whether materials and/or products of LOTTE Chemical and/or a design that uses or utilizes LOTTE Chemical’ recommendations or proposals are (is) compatible with individual uses shall be determined solely by each user and such user shall be solely responsible for any results, including but not limited to, any and all loss and damages incurred due to such uses. Users must implement and verify all testing and analyses for proving the safety and compatibility of final products that have been created or altered by using LOTTE Chemical’ materials or products. The data and values inserted and/or contained in this document may be changed due to quality improvement of the product without any prior notification.
* The last update date : 2024/01/24